Authors: Vecchietti, J; Lustemberg, P; Fornero, EL; Calatayud, M; Collins, SE; Mohr, S; Ganduglia-Pirovano, MV; Libuda, J; Bonivardi, AL

Appl. Catal. B-Environ.. vol: 277. page: 0926-3373.
Date: nov-15. 2020.
Doi: 10.1016/j.apcatb.2020.119103.

The ethanol steam reforming reaction, together with the adsorption and decomposition of ethanol was studied on CeO2 and gallium-doped ceria (CeGaOx) by a combined experimental and theoretical approach using infrared spectroscopy (IR), mass spectrometry (MS) and density functional theory (DFT) calculations. At 100 degrees C, different types of monodentate ethoxy species were identified as standing-up (SU) on Ce4+ and lying-down (LD) on Ce4+ and Ga3+, with the alkyl chain more perpendicular or parallel to the surface, respectively. It is suggested that the incorporation of Ga into the ceria lattice changes the decomposition pathway of LD species, which converts to acetate instead of ethylene, attributed to the increased lattice oxygen lability in the Ce-O-Ga interface upon doping and the propensity to form Ga-H surface species. Under ethanol steam reforming conditions, Ga doping of ceria-based materials has a drastic effect by improving the H-2:CO2 ratio, changing the product distribution and reducing coke formation..